Front carrier
Rear carrier
| Tensile strength | 0.2% proof stress | Elongation | Young's modulus | Linear expansion coefficient | Castability | Corrosion resistance | Specific gravity | |
|---|---|---|---|---|---|---|---|---|
| MPa | MPa | % | GPa | 10-6/℃ | ||||
| NH41-F | 317 | 247 | 0.6 | 81 | 19.4 | 4 | 1 | 2.70 |
| NH41-T5 | 338 | 327 | 0.1 | 81 | ||||
| ADC14-F | 260 | 258 | 0.4 | 81 | 19.0 | 3 | 1 | 2.70 |
| ADC12-F | 296 | 186 | 2.0 | 71 | 21.0 | 5 | 1 | 2.73 |
* Evaluated using 6 mm plate PDF samples.
* The mechanical properties of ADC14 and ADC12 are quoted from the material database of the Japan Aluminum Association.
* Use this data as reference values.
| Tensile strength | 0.2% proof stress | Elongation | Young's modulus | Linear expansion coefficient | Castability | Corrosion resistance | Specific gravity | |
|---|---|---|---|---|---|---|---|---|
| MPa | MPa | % | GPa | 10-6/℃ | ||||
| NH42-F | 265 | 168 | 1.3 | 80 | 19.4 | 4 | 1 | 2.70 |
| NH42-T6 | 381 | 346 | 0.7 | 80 | ||||
| A390-F | 242 | 195 | 0.5 | 81 | 19.0 | 3 | 1 | 2.68 |
| A390-T6 | 385 | 383 | 0.3 | 81 |
* Measured using die gravity casting samples.
* Use this data as reference values
Primary Si crystals of 50 μm or more are unevenly distributed in ADC14, but primary Si crystals of 20 to 30 μm are uniformly dispersed in NH41.
Wear resistance:
NH41 = ADC14 (B390) > ADC12